A calender is a series of hard pressure rollers used to finish or smooth a sheet of material such as paper, textiles, or plastics. Calender rolls are also used to form some types of plastic films and to apply coatings. Some calender rolls are heated or cooled as needed. Calenders are sometimes mis-spelled calendars.
In eighteenth century China, workers called "calenderers" in the silk and cotton cloth trades, used heavy rollers to press and finish cloth.
In 1836, Edwin M. Chaffee, of the Roxbury India Rubber Company, patented a four-roll calender to make rubber sheet. Chaffee worked with Charles Goodyear with the intention to "produce a sheet of rubber laminated to a fabric base". Calenders were also used for paper and fabrics long before later applications for thermoplastics. With the expansion of the rubber industry the design of calenders grew as well, so when PVC was introduced the machinery was already capable of processing it into film. As recorded in an overview on the history of the development of calenders, "There was development in both Germany and the United States and probably the first successful calendering of PVC was in 1935 in Germany, where in the previous year the Hermann Berstorff Company of Hannover designed the first calender specifically to process this plastic".
In the past, for paper, sheets were worked on with a polished hammer or pressed between polished metal sheets in a press. With the continuously operating paper machine it became part of the process of rolling the paper (in this case also called web paper). The pressure between the rollers, the "nip pressure", can be reduced by heating the rolls or moistening the paper surface. This helps to keep the bulk and the stiffness of the web paper which is beneficial for its later use.
Modern calenders have "hard" heated rollers made from chilled cast iron or steel, and "soft" rollers coated with polymeric composites. The soft roller is slightly non-cylindrical, tapered in diameter toward both ends, to widen the working nip and distribute the specific pressure on the paper more evenly.
In a principal paper application, the calender is located at the end of a papermaking process (on-line). Those that are used separately from the process (off-line) are also called supercalenders. The purpose of a calender is to make the paper smooth and glossy for printing and writing, as well as of a consistent thickness for capacitors that use paper as their dielectric membrane.
The calender section of a paper machine consists of a calender and other equipment. The paper web is run between in order to further smooth it out, which also gives it a more uniform thickness. The pressure applied to the web by the rollers determines the finish of the paper, and there are three types of finish that the paper can have.
The first is Machine Finish, or MF Paper and it can range from a Rough/ Matt (non glossy) look, to a Smooth high quality finish.
The second is called a Supercalendered Finish, or MG Paper (Machine Glazed) which is Glossy/ Glazed, suitable for a high degree fine-screened halftone printing.
The third type of finish is called a plater finish, and whereas the first two types of finish are accomplished by the calender stack itself, a plater finish is obtained by placing cut sheets of paper between zinc or copper plates that are stacked together, then put under pressure and heating. A special finish such as a linen finish would be achieved by placing a piece of linen between the plate and the sheet of paper, or else an embossed steel roll might be used.
After calendering, the web has a moisture content of about 6% (depending on the furnish). It is wound onto a roll called a tambour, and stored for final cutting and shipping.
A supercalender is a stack of calenders consisting of alternating steel and fiber-covered rolls through which paper is passed to increase its density, smoothness and gloss. It is similar to a calender except that alternate chilled cast iron and softer rolls are used. The rolls used to supercalender uncoated paper usually consist of cast iron and highly compressed paper, while the rolls used for coated paper are usually cast iron and highly compressed cotton. The finish produced varies according to the raw material used to make the paper and the pressure exerted on it, and ranges from the highest English finish to a highly glazed surface. Supercalendered papers are sometimes used for books containing fine line blocks or halftones because they print well from type and halftones, although for the latter they are not as good as coated paper.
Calendering is a finishing process used on cloth and fabrics. A calender is employed, usually to smooth, coat, or thin a material.
With textiles, fabric is passed under rollers at high temperatures and pressures. Calendering is used on fabrics such as moire to produce its watered effect and also on cambric and some types of sateens.
Calenders can also be applied to materials other than paper when a smooth, flat surface is desirable, such as cotton, linens, silks, and various man-made fabrics and polymers such as vinyl and ABS polymer sheets, and to a lesser extent HDPE, polypropylene and polystyrene.
The calender is also an important processing machine in the rubber industries, especially in the manufacture of tires, where it is used for the inner layer and fabric layer.
Calendering can also used for polishing, or making uniform, coatings applied to substrates- an older use was in polishing magnetic tapes, for which the contact roller rotates much faster than the web speed. More recently, it is used in the production of certain types of secondary battery cells (such as spirally-wound or prismatic Lithium-ion cells) to achieve uniform thickness of electrode material coatings on current collector foils.
- US5167894A, Wilfried W. Baumgarten, "Apparatus comprising an extruder and a calender for producing sheets and/or foils from plastic or rubber mixtures", published 1992
- US4425489A, Pav, Lauscher, "Electromagnetic heating system for calender rolls or the like", published 1984
- "Definition of CALENDER". www.merriam-webster.com.
- White, James Lindsay (July 20, 1990). Principles of Polymer Engineering Rheology. Wiley-Interscience. p. 49. Retrieved 2014-12-25.
- Simpson, W. G. (December 31, 1995). Plastics: Surface and Finish. Royal Society of Chemistry. p. 52. Retrieved 2014-12-25.
- "Archived copy". Archived from the original on 2009-04-10. Retrieved 2018-11-17.CS1 maint: archived copy as title (link)
- Westerlund Leslie. C. " How to Make Smooth Papermaking Technology" ISBN 1-876141-55-7;Westerlund Eco Services; Rockingham; W.Australia. 2008.
- Hawkins, William E, The Plastic Film and Foil Web Handling Guide CRC Press 2003
- Jenkins, W. A., and Osborn, K. R. Plastic Films: Technology and Packaging Applications, CRC Press 1992
- Yam, K. L., "Encyclopedia of Packaging Technology", John Wiley & Sons, 2009, ISBN 978-0-470-08704-6