Brinell scale

The Brinell scale /brəˈnɛl/ characterizes the indentation hardness of materials through the scale of penetration of an indenter, loaded on a material test-piece. It is one of several definitions of hardness in materials science.


Proposed by Swedish engineer Johan August Brinell in 1900, it was the first widely used and standardised hardness test in engineering and metallurgy. The large size of indentation and possible damage to test-piece limits its usefulness. However it also had the useful feature that the hardness value divided by two gave the approximate UTS in ksi for steels. This feature contributed to its early adoption over competing hardness tests.

Test details

The typical test uses a 10 mm (0.39 in) diameter steel ball as an indenter with a 3,000 kgf (29.42 kN; 6,614 lbf) force. For softer materials, a smaller force is used; for harder materials, a tungsten carbide ball is substituted for the steel ball. The indentation is measured and hardness calculated as:


BHN = Brinell Hardness Number (kgf/mm2)
P = applied load in kilogram-force (kgf)
D = diameter of indenter (mm)
d = diameter of indentation (mm)

Brinell hardness is sometimes quoted in megapascals; the Brinell hardness number is multiplied by the acceleration due to gravity, 9.80665 m/s2, to convert it to megapascals.

The BHN can be converted into the ultimate tensile strength (UTS), although the relationship is dependent on the material, and therefore determined empirically. The relationship is based on Meyer's index (n) from Meyer's law. If Meyer's index is less than 2.2 then the ratio of UTS to BHN is 0.36. If Meyer's index is greater than 2.2, then the ratio increases.[1]

BHN is designated by the most commonly used test standards (ASTM E10-14[2] and ISO 6506–1:2005[3]) as HBW (H from hardness, B from brinell and W from the material of the indenter, tungsten (wolfram) carbide). In former standards HB or HBS were used to refer to measurements made with steel indenters.

HBW is calculated in both standards using the SI units as


F = applied load (newtons)
D = diameter of indenter (mm)
d = diameter of indentation (mm)

Common values

When quoting a Brinell hardness number (BHN or more commonly HB), the conditions of the test used to obtain the number must be specified. (HB is not related to the "HB" degree of pencil hardness.) The standard format for specifying tests can be seen in the example "HBW 10/3000". "HBW" means that a tungsten carbide (from the chemical symbol for tungsten or from the Swedish/German name for tungsten, "Wolfram") ball indenter was used, as opposed to "HBS", which means a hardened steel ball. The "10" is the ball diameter in millimeters. The "3000" is the force in kilograms force.

The hardness may also be shown as XXX HB YYD2. The XXX is the force to apply (in kgf) on a material of type YY (5 for aluminum alloys, 10 for copper alloys, 30 for steels). Thus a typical steel hardness could be written: 250 HB 30D2. It could be a maximum or a minimum.

Correspondent relations among scale, indenter and test force:
Hardness symbol Diameter of Indenter


F/D2 Test force


HBW 10/3000 10 30 29420(3000)
HBW 10/1500 10 15 14710(1500)
HBW 10/1000 10 10 9807(1000)
Brinell hardness numbers
Softwood (e.g., pine)1.6 HBS 10/100
Hardwood2.6–7.0 HBS 1.6 10/100
Lead5.0 HB (pure lead; alloyed lead typically can range from 5.0 HB to values in excess of 22.0 HB)
Pure Aluminium15 HB
Copper35 HB
Hardened AW-6060 Aluminium75 HB
Mild steel120 HB
18–8 (304) stainless steel annealed200 HB[4]
Hardox wear plate400-700 HB
Hardened tool steel600–900 HB (HBW 10/3000)
Glass1550 HB
Rhenium diboride4600 HB
Note: Standard test conditions unless otherwise stated


See also


  1. Tabor 2000, p. 17.
  2. ASTM E10-14.
  3. EN ISO 6506-1:2005.
  4. "AISI Type 304 Stainless Steel". ASM Material Data Sheet. n.d. Retrieved 28 May 2019.