Surface finishing is a broad range of industrial processes that alter the surface of a manufactured item to achieve a certain property. Finishing processes may be employed to: improve appearance, adhesion or wettability, solderability, corrosion resistance, tarnish resistance, chemical resistance, wear resistance, hardness, modify electrical conductivity, remove burrs and other surface flaws, and control the surface friction. In limited cases some of these techniques can be used to restore original dimensions to salvage or repair an item. An unfinished surface is often called mill finish.
Surface finishing processes can be categorized by how they affect the workpiece:
- Removing or reshaping finishing
- Adding or altering finishing
Mechanical processes may also be categorized together because of similarities the final surface finish.
Adding and altering
- Case hardening
- Ceramic glaze
- Corona treatment
- Diffusion processes:
- Electroless plating
- Passivation/Conversion coating
- Plasma spraying
- Powder coating
- Thin-film deposition
- Vitreous enamel
Removing and reshaping
- Abrasive blasting
- Chemical-mechanical planarization (CMP)
- Flame polishing
- Gas cluster ion beam
- Industrial etching
- Laser ablation
- Laser engraving
- Magnetic field-assisted finishing
- Mass finishing processes processes
- Abrasive blasting
- Mass finishing
Metal finish designations
- #3 Finish
Also known as grinding, roughing or rough grinding. These finishes are coarse in nature and usually are a preliminary finish applied before manufacturing. An example would be grinding gates off of castings, deburring or removing excess weld material. It is coarse in appearance and applied by using 36–100 grit abrasive.
When the finish is specified as #3, the material is polished to a uniform 60–80 grit.
- #4 Architectural finish
Also known as brushed, directional or satin finish. A #4 architectural finish is characterized by fine polishing grit lines that are uniform and directional in appearance. It is produced by polishing the metal with a 120–180 grit belt or wheel finish and then softened with an 80–120 grit greaseless compound or a medium non woven abrasive belt or pad.
- #4 Dairy or sanitary finish
This finish is commonly used for the medical and food industry and almost exclusively used on stainless steel. This finish is much finer than a #4 architectural finish. This finish enhances the physical appearance of the metal as well as increases the sanitary benefits. One takes great care to remove any surface defects in the metal, like pits, that could allow bacteria to grow. A #4 dairy or sanitary finish is produced by polishing with a 180–240 grit belt or wheel finish softened with 120–240 grit greaseless compound or a fine non woven abrasive belt or pad.
- #6 Finish
Also known as a fine satin finish. This finish is produced by polishing with a 220–280 grit belt or wheel softened with a 220–230 greaseless compound or very fine non woven abrasive belt or pad. Polishing lines will be soft and less reflective than a #4 architectural finish.
- #7 Finish
A #7 finish is produced by polishing with a 280–320 belt or wheel and sisal buffing with a cut and color compound. This is a semi-bright finish that will still have some polishing lines but they will be very dull. Carbon steel and iron are commonly polished to a #7 finish before chrome plating. A #7 finish can be made bright by color buffing with coloring compound and a cotton buff. This is commonly applied to keep polishing costs down when a part needs to be shiny but not flawless.
- #8 Finish
Also known as a mirror finish. This finish is produced by polishing with at least a 320 grit belt or wheel finish. Care will be taken in making sure all surface defects are removed. The part is sisal buffed and then color buffed to achieve a mirror finish. The quality of this finish is dependent on the quality of the metal being polished. Some alloys of steel and aluminum cannot be brought to a mirror finish. Castings that have slag or pits will also be difficult, if not impossible, to polish to a #8.
- Degarmo, E. Paul; Black, J T.; Kohser, Ronald A. (2003), Materials and Processes in Manufacturing (9th ed.), Wiley, ISBN 0-471-65653-4.